RTP 208 K
Polyarylamide
45% Glass Fiber
Product Description
Warning: The status of this material is 'Commercial: Limited Issue'

The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade.
General
Filler / Reinforcement	Glass Fiber, 45% Filler by Weight

RoHS Compliance	Contact Manufacturer

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.58	g/cm³	ASTM D792
Molding Shrinkage - Flow (3.18 mm)	0.10 to 0.20	%	ASTM D955
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	17600	MPa	ASTM D638
Tensile Strength	234	MPa	ASTM D638
Tensile Elongation (Yield)	2.0 to 3.0	%	ASTM D638
Flexural Modulus	17200	MPa	ASTM D790
Flexural Strength	333	MPa	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	88	J/m	ASTM D256
Unnotched Izod Impact (3.18 mm)	720	J/m	ASTM D4812
Flammability	Nominal Value		Test Method
Flame Rating (1.50 mm, Values per RTP Company testing.)	HB		UL 94
Injection	Nominal Value	Unit
Drying Temperature	121	°C
Drying Time	4.0 to 5.0	hr
Processing (Melt) Temp	249 to 282	°C
Mold Temperature	121 to 141	°C
Injection Pressure	82.7 to 124	MPa
Injection Notes
Desiccant Type Dryer Required.