| Reny® NXG5945S | |||
| Polyarylamide | |||
| 45% Glass Fiber | |||
| Product Description | |||
| Reny® NXG5945S is a Polyarylamide (PARA) material filled with 45% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® NXG5945S: Flame Rated. | |||
| General | |||
| UL Yellow Card 2 | E41179-535314 | ||
| Filler / Reinforcement | Glass Fiber, 45% Filler by Weight | ||
| Processing Method | Injection Molding | ||
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.52 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 13 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 8.5 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.32 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.73 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus | 16000 | 15400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 208 | 202 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2 | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 14300 | 14000 | MPa | ISO 178 |
| Flexural Stress | 349 | 315 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 15 | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 90 | 77 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 232 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature | 87 | -- | °C | ISO 11357-2 |
| Melting Temperature | 257 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.10E-05 | -- | cm/cm/°C | |
| Transverse | 5.60E-05 | -- | cm/cm/°C | |
| Electrical | Dry | Conditioned | Test Method | |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.2 | 4.6 | ||
| 1 MHz | 4.1 | 4.2 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.50E-03 | 0.02 | ||
| 1 MHz | 6.70E-03 | 0.012 | ||
| Flammability | Dry | Conditioned | Test Method | |
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Injection | Dry | Unit | ||
| Drying Temperature | ||||
| A | 120 | °C | ||
| B | 80 | °C | ||
| Drying Time | ||||
| A | > 3.0 | hr | ||
| B | > 12 | hr | ||
| Rear Temperature | 280 | °C | ||
| Middle Temperature | 285 | °C | ||
| Front Temperature | 290 | °C | ||
| Nozzle Temperature | 290 | °C | ||
| Mold Temperature | 120 to 140 | °C | ||
| Injection Pressure | 20.0 to 150 | MPa | ||
| Injection Rate | Moderate-Fast | |||
| Screw Speed | 60 to 150 | rpm |