PARA Reny® F34S

2019-04-18

Reny® F34S
Polyarylamide
30% Whisker
Product Description
Reny® F34S is a Polyarylamide (PARA) material filled with 30% whisker. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® F34S are:

Flame Rated

Wear Resistant

General
UL Yellow Card²	E41179-231788

Filler / Reinforcement	Whisker, 30% Filler by Weight

Features	Good Wear Resistance	Low Friction

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.59	g/cm³	ISO 1183
Molding Shrinkage	0.59	%
Water Absorption (Saturation, 23°C)	0.23	%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11400	MPa	ISO 527-2
Tensile Stress (Break)	102	MPa	ISO 527-2
Tensile Strain (Break)	1	%	ISO 527-2
Flexural Modulus	12300	MPa	ISO 178
Flexural Stress	217	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	2.4	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	25	kJ/m²	ISO 179
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	206	°C	ISO 75-2/A
Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94
Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	280	°C
Middle Temperature	285	°C
Front Temperature	290	°C
Nozzle Temperature	290	°C
Mold Temperature	80.0 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm