PARA Reny® C-408
2019-04-18
Reny® C-408 |
|
|
|
Polyarylamide |
|
|
|
40% Long Carbon Fiber |
|
|
|
Product Description |
Reny® C-408 is a Polyarylamide (PARA) material filled with 40% long carbon fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® C-408: Flame Rated. |
General |
|
Filler / Reinforcement |
Long Carbon Fiber, 40% Filler by Weight |
Processing Method |
Injection Molding |
Physical |
Dry |
Conditioned |
Unit |
Test Method |
Density |
1.38 |
-- |
g/cm³ |
ISO 1183 |
Molding Shrinkage |
0.28 |
-- |
% |
|
Water Absorption (Equilibrium, 23°C, 50% RH) |
2.3 |
-- |
% |
ISO 62 |
Mechanical |
Dry |
Conditioned |
Unit |
Test Method |
Tensile Modulus |
34200 |
29900 |
MPa |
ISO 527-2 |
Tensile Stress (Break) |
287 |
251 |
MPa |
ISO 527-2 |
Tensile Strain (Break) |
0.9 |
1 |
% |
ISO 527-2 |
Flexural Modulus |
33000 |
31000 |
MPa |
ISO 178 |
Flexural Stress |
500 |
450 |
MPa |
ISO 178 |
Impact |
Dry |
Conditioned |
Unit |
Test Method |
Charpy Notched Impact Strength (23°C) |
19 |
13 |
kJ/m² |
ISO 179 |
Charpy Unnotched Impact Strength (23°C) |
46 |
43 |
kJ/m² |
ISO 179 |
Thermal |
Dry |
Conditioned |
Unit |
Test Method |
Heat Deflection Temperature |
|
|
|
|
0.45 MPa, Unannealed |
238 |
238 |
°C |
ISO 75-2/B |
1.8 MPa, Unannealed |
234 |
226 |
°C |
ISO 75-2/A |
Flammability |
Dry |
Conditioned |
|
Test Method |
Flame Rating |
HB |
-- |
|
UL 94 |
Injection |
Dry |
Unit |
|
|
Drying Temperature |
|
|
|
|
A |
120 |
°C |
|
|
B |
80 |
°C |
|
|
Drying Time |
|
|
|
|
A |
> 3.0 |
hr |
|
|
B |
> 12 |
hr |
|
|
Rear Temperature |
270 |
°C |
|
|
Middle Temperature |
275 |
°C |
|
|
Front Temperature |
280 |
°C |
|
|
Nozzle Temperature |
280 |
°C |
|
|
Mold Temperature |
120 to 140 |
°C |
|
|
Injection Pressure |
20.0 to 150 |
MPa |
|
|
Injection Rate |
Moderate-Fast |
|
|
|
Screw Speed |
60 to 150 |
rpm |
|
|