PARA Reny® 4501

2018-12-18

Reny® 4501
Polyarylamide
30% Glass Fiber
Product Description
Reny® 4501 is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 4501 are:

Flame Rated

Flame Retardant

Conductive

General
UL Yellow Card²	E41179-231772

Filler / Reinforcement	Glass Fiber, 30% Filler by Weight

Additive	Flame Retardant

Features	Electrically Conductive	Flame Retardant

Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.66	--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/2.10 kg)	10	--	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (275°C/2.10 kg)	7.5	--	cm³/10min	ISO 1133
Molding Shrinkage	0.3	--	%
Water Absorption				ISO 62
Saturation, 23°C	0.06	--	%
Equilibrium, 23°C, 50% RH	0.8	--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	20400	16200	MPa	ISO 527-2
Tensile Stress (Break)	107	113	MPa	ISO 527-2
Tensile Strain (Break)	0.7	0.9	%	ISO 527-2
Flexural Modulus	19100	15500	MPa	ISO 178
Flexural Stress	190	184	MPa	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	7.5	6.6	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	14	15	kJ/m²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	236	232	°C	ISO 75-2/B
1.8 MPa, Unannealed	225	216	°C	ISO 75-2/A
Flammability	Dry	Conditioned		Test Method
Flame Rating (1.60 mm)	V-0	--		UL 94
Injection	Dry	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	260	°C
Middle Temperature	265	°C
Front Temperature	270	°C
Nozzle Temperature	270	°C
Mold Temperature	120 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm