PARA Reny® 2620

2018-09-05

Reny® 2620
Polyarylamide
20% Glass\Mineral
Product Description
Reny® 2620 is a Polyarylamide (PARA) material filled with 20% glass\mineral. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 2620 are:

Flame Rated

Warp Resistant

General
UL Yellow Card²	E41179-231764

Filler / Reinforcement	Glass\Mineral, 20% Filler by Weight

Features	Low Warpage

Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.66	--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg)	18	--	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg)	12.3	--	cm³/10min	ISO 1133
Molding Shrinkage	0.46	--	%
Water Absorption				ISO 62
Saturation, 23°C	0.14	--	%
Equilibrium, 23°C, 50% RH	1.3	--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	17600	11500	MPa	ISO 527-2
Tensile Stress (Break)	139	86	MPa	ISO 527-2
Tensile Strain (Break)	1.1	1.3	%	ISO 527-2
Flexural Modulus	16000	10900	MPa	ISO 178
Flexural Stress	236	151	MPa	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.1	5.1	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	27	35	kJ/m²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	234	231	°C	ISO 75-2/B
1.8 MPa, Unannealed	214	196	°C	ISO 75-2/A
CLTE				ISO 11359-2
Flow	1.00E-05	--	cm/cm/°C
Transverse	4.00E-05	--	cm/cm/°C
Flammability	Dry	Conditioned		Test Method
Flame Rating (1.60 mm)	HB	--		UL 94
Injection	Dry	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	270	°C
Middle Temperature	275	°C
Front Temperature	280	°C
Nozzle Temperature	280	°C
Mold Temperature	120 to 140	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm