PARA Reny® 1511AH

2018-09-05

Reny® 1511AH
Polyarylamide
40% Glass Fiber
Product Description
Reny® 1511AH is a Polyarylamide (PARA) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding.

Important attributes of Reny® 1511AH are:

Flame Rated

Flame Retardant

General
UL Yellow Card²	E41179-231749

Filler / Reinforcement	Glass Fiber, 40% Filler by Weight

Additive	Flame Retardant

Features	Flame Retardant

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.65	g/cm³	ISO 1183
Molding Shrinkage	0.49	%
Water Absorption			ISO 62
Saturation, 23°C	0.15	%
Equilibrium, 23°C, 50% RH	1.1	%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	16500	MPa	ISO 527-2
Tensile Stress (Break)	197	MPa	ISO 527-2
Tensile Strain (Break)	2	%	ISO 527-2
Flexural Modulus	15000	MPa	ISO 178
Flexural Stress	302	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	45	kJ/m²	ISO 179
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	237	°C	ISO 75-2/B
1.8 MPa, Unannealed	224	°C	ISO 75-2/A
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	6.00E+15	ohms	IEC 60093
Volume Resistivity	7.00E+16	ohms·cm	IEC 60093
Electric Strength			IEC 60243-1
1.00 mm	33	kV/mm
2.00 mm	24	kV/mm
Relative Permittivity (1 MHz)	4		IEC 60250
Dissipation Factor (1 MHz)	9.00E-03		IEC 60250
Comparative Tracking Index	325	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-0		UL 94
Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
B	80	°C
Drying Time
A	> 3.0	hr
B	> 12	hr
Rear Temperature	260	°C
Middle Temperature	265	°C
Front Temperature	270	°C
Nozzle Temperature	270	°C
Mold Temperature	120 to 145	°C
Injection Pressure	20.0 to 150	MPa
Injection Rate	Moderate-Fast
Screw Speed	60 to 150	rpm