PARA Reny® 1371
2018-09-05
Reny® 1371 |
|
|
|
Polyarylamide |
|
|
|
55% Glass Fiber |
|
|
|
Product Description |
Reny® 1371 is a Polyarylamide (PARA) material filled with 55% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. |
|
Important attributes of Reny® 1371 are: |
|
Flame Rated |
|
Impact Resistant |
|
General |
|
UL Yellow Card 2 |
E41179-507088 |
Filler / Reinforcement |
Glass Fiber, 55% Filler by Weight |
Features |
High Impact Resistance |
Processing Method |
Injection Molding |
Physical |
Nominal Value |
Unit |
Test Method |
Density |
1.66 |
g/cm³ |
ISO 1183 |
Molding Shrinkage |
0.4 |
% |
|
Water Absorption |
|
|
ISO 62 |
Saturation, 23°C |
0.11 |
% |
|
Equilibrium, 23°C, 50% RH |
0.9 |
% |
|
Mechanical |
Nominal Value |
Unit |
Test Method |
Tensile Modulus |
20800 |
MPa |
ISO 527-2 |
Tensile Stress (Break) |
242 |
MPa |
ISO 527-2 |
Tensile Strain (Break) |
1.9 |
% |
ISO 527-2 |
Flexural Modulus |
19600 |
MPa |
ISO 178 |
Flexural Stress |
403 |
MPa |
ISO 178 |
Impact |
Nominal Value |
Unit |
Test Method |
Charpy Notched Impact Strength (23°C) |
16 |
kJ/m² |
ISO 179 |
Charpy Unnotched Impact Strength (23°C) |
93 |
kJ/m² |
ISO 179 |
Thermal |
Nominal Value |
Unit |
Test Method |
Heat Deflection Temperature |
|
|
|
0.45 MPa, Unannealed |
236 |
°C |
ISO 75-2/B |
1.8 MPa, Unannealed |
227 |
°C |
ISO 75-2/A |
Flammability |
Nominal Value |
|
Test Method |
Flame Rating |
|
|
UL 94 |
-- |
HB |
|
|
1.60 mm |
HB |
|
|
Injection |
Nominal Value |
Unit |
|
Drying Temperature |
|
|
|
A |
120 |
°C |
|
B |
80 |
°C |
|
Drying Time |
|
|
|
A |
> 3.0 |
hr |
|
B |
> 12 |
hr |
|
Rear Temperature |
270 |
°C |
|
Middle Temperature |
275 |
°C |
|
Front Temperature |
280 |
°C |
|
Nozzle Temperature |
280 |
°C |
|
Mold Temperature |
120 to 140 |
°C |
|
Injection Pressure |
20.0 to 150 |
MPa |
|
Injection Rate |
Moderate-Fast |
|
|
Screw Speed |
60 to 150 |
rpm |
|