LUVOCOM® 16-8960/ES      
Polyarylamide      
Carbon Fiber; Steel      
Product Description
LUVOCOM® 16-8960/ES is a Polyarylamide (PARA) material filled with carbon fiber and steel. It is available in Europe.
 
Important attributes of LUVOCOM® 16-8960/ES are:
 
Conductive
 
Electromagnetic Shielding (EMI)
 
ESD Protection
 
Good Stiffness
 
Moisture Resistant
 
 
Typical applications include:
 
Engineering/Industrial Parts
 
Automotive
 
Business/Office Goods
 
Fabrics/Fibers
 
Handles
 
General  
Material Status  Commercial: Active
Filler / Reinforcement  Carbon Fiber Steel  
Features  Electrically Conductive ESD Protection Good Strength
     
Electromagnetic Shielding (EMI) Good Stiffness Low to No Water Absorption
     
Uses  Automotive Applications Handles Textile Applications
   
Business Equipment Housings
   
Engineering Parts Rollers
   
Appearance  Black

Physical Nominal Value Unit Test Method
Density 1.41 g/cm³ ISO 1183
Molding Shrinkage 0.20 to 0.60 % DIN 16901
Water Absorption (23°C, 24 hr) < 0.30 % 　
Mechanical Nominal Value Unit Test Method
Tensile Modulus 10000 MPa ISO 527-2
Tensile Stress (Break) 125 MPa ISO 527-2
Tensile Strain (Yield) 1.6 % ISO 527-2
Flexural Modulus 9000 MPa ISO 178
Flexural Stress 180 MPa ISO 178
Flexural Strain at Flexural Strength 2.1 % ISO 178
Impact Nominal Value Unit Test Method
Charpy Unnotched Impact Strength 　 　 　
-30°C 19 kJ/m² ISO 179/1fU
23°C 20 kJ/m² ISO 179/1eU
Thermal Nominal Value Unit Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed) 230 °C ISO 75-2/A
Continuous Use Temperature 120 °C UL 746B
Maximum Use Temperature - Short Term  160 °C 　
Electrical Nominal Value Unit Test Method
Surface Resistivity < 1.0E+2 ohms IEC 60093
Insulation Resistance < 10 ohms IEC 60167
Injection Nominal Value Unit 　
Drying Temperature 　 　 　
B  130 °C 　
Desiccant Dryer, A  100 °C 　
Drying Time 　 　 　
B  4.0 to 6.0 hr 　
Desiccant Dryer, A  6.0 to 8.0 hr 　
Suggested Max Moisture 0.1 % 　
Rear Temperature 260 to 300 °C 　
Middle Temperature 260 to 300 °C 　
Front Temperature 260 to 300 °C 　
Nozzle Temperature 250 to 290 °C 　
Processing (Melt) Temp 285 °C 　
Mold Temperature 110 to 140 °C 　
Injection Notes
General
　
In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines.
　
Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials.
　
Lengthy dwell times for the melts in the cylinder should be avoided.
　
Lower the temperatures during interruptions!
　
　
Predrying (optional)
　
It is advisable to predry the granulate with a suitable dryer immediately before processing.
　
The granulate may absorb moisture from the air.
　
　
Delivery Form & Storage
　
Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets.
　
Preferably storage should be effected in dry and normally temperatured rooms
　
　
Additional Information
　
During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration.
　
The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application.
　
Please contact us for further information.