| Ixef® FC-1022 | |||
| 聚丙烯酰胺 | |||
| 50% 玻璃纤维增强材料 | |||
| 产品说明 | |||
| Ixef® FC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance. | |||
| Ixef® FC-1022 is approved for food contact and meets FDA regulations for Ixef® FC-1022 NT 000 (natural) and Ixef® FC-1022 BK 000 (black) based on clearances granted by FCN 001242 for repeated use food contact applications with all food types, under FDA conditions of use B through H as described in Tables 1 and 2 of 21 CFR 176.170(c). | |||
| Black: FC-1022 BK 000 | |||
| Natural: FC-1022 NT 000 | |||
| 总体 | |||
| UL 黄卡 2 | E95746-101810229 | ||
| 填料/增强材料 | 玻璃纤维增强材料, 50% 填料按重量 | ||
| 特性 | 超强刚性 | 高强度 | 耐化学性良好 |
| 尺寸稳定性良好 | 好的消毒性 | 食品接触的合规性 | |
| 出色的外观 | 良好的抗蠕变性 | 通用 | |
| 低吸湿性 | 流动性高 | ||
| 用途 | 电器用具 | 食品服务领域 | |
| 高光应用 | 医疗器材 | ||
| 机构评级 | FDA 21 CFR 176.170(c) 3 | 欧洲 10/1/2011 12:00:00 AM | |
| RoHS 合规性 | RoHS 合规 | ||
| 外观 | 黑色 | 自然色 | |
| 形式 | 粒子 | ||
| 加工方法 | 注射成型 | ||
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 | 1.64 | -- | g/cm³ | ISO 1183 |
| 收缩率 | 0.10 到 0.30 | -- | % | ISO 294-4 |
| 吸水率 (23°C, 24 hr) | 0.16 | -- | % | ISO 62 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量 | 19500 | 19500 | MPa | ISO 527-2 |
| 拉伸应力 (断裂) | 280 | 260 | MPa | ISO 527-2 |
| 拉伸应变 (断裂) | 1.9 | 2.2 | % | ISO 527-2 |
| 弯曲模量 | 18500 | -- | MPa | ISO 178 |
| 弯曲应力 | 380 | -- | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 悬壁梁缺口冲击强度 | 110 | -- | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 | 850 | -- | J/m | ASTM D256 |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 热变形温度 (1.8 MPa, 未退火) | 230 | -- | °C | ISO 75-2/A |
| 线形热膨胀系数 - 流动 | 1.50E-05 | -- | cm/cm/°C | ISO 11359-2 |
| 补充信息 | 干燥 | 调节后的 | ||
| 吸水性 - Equil, 65% RH | -- | |||
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 | 120 | °C | ||
| 干燥时间 | 0.50 到 1.5 | hr | ||
| 料筒后部温度 | 250 到 260 | °C | ||
| 料筒前部温度 | 260 到 290 | °C | ||
| 射嘴温度 | 260 到 290 | °C | ||
| 加工（熔体）温度 | 280 | °C | ||
| 模具温度 | 120 到 140 | °C | ||
| 注射速度 | 快速 | |||
| 注射说明 | ||||
| Hot runners: 250°C to 260°C (482°C to 500°F) | ||||
| Storage | ||||
| Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef® processing guide. | ||||
| Drying | ||||
| The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). | ||||
| Injection Molding | ||||
| Ixef® FC-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. | ||||
| The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F). | ||||
| To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%). | ||||
| 备注 | ||||
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 | ||||
| 2UL 黄卡含有 UL 验证的易燃性和电气特性。UL Prospector 持续努力在 Prospector 中将黄卡链接至单个塑料材料，然而此列表可能未包括所有相应链接。重要的是，我们对 Prospector 中找到的这些黄卡和塑料材料之间的关联进行验证。如需完整的黄卡列表，请访问 UL 黄卡搜索。 | ||||
| 3FDA conditions of use B through H as described in Tables 1 and 2 of 21CFR 176.170(c). | ||||
| Ixef® GS-1022 | ||||
| 聚丙烯酰胺 | ||||
| 50% 玻璃纤维增强材料 | ||||
| 产品说明 | ||||
| Ixef® GS-1022 is a 50% glass-fiber reinforced grade of polyarylamide (PARA) available in several colors. Parts molded from these colored resins can withstand high-energy gamma radiation without significant change in appearance and physical properties. Ixef® GS-1022 resins demonstrate no evidence of cytotoxicity, sensitization, intracutaneous reactivity or acute systemic toxicity, based on biocompatibility testing as defined by ISO 10993-1. | ||||
| This resin offers superior strength and stiffness combined with outstanding surface gloss and exceptional flow and is well suited for medical applications, such as single use surgical instruments and structural device housings, and applications in food service equipment. | ||||
| Colors available: | ||||
| Brown: GS-1022 BN01 | ||||
| Blue: GS-1022 BU01 | ||||
| Green: GS-1022 GN01 | ||||
| Grey: GS-1022 GY01 | ||||
| Grey: GS-1022 GY02 | ||||
| Grey: GS-1022 GY51 | ||||
| White: GS-1022 WH01 | ||||