Stanyl® ForTii™ K12Polyamide 4T
40% Glass Fiber
DSM Engineering Plastics
Product Description:
For E&E applications
|
General
|
||||
| Filler / Reinforcement | Glass Fiber, 40% Filler by Weight | |||
| Forms | Pellets | |||
| Processing Method | Injection Molding | |||
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.51 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1 | -- | % | |
| Flow | 0.35 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus | 13500 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2 | -- | % | ISO 527-2 |
| Flexural Modulus | 13500 | -- | MPa | ISO 178 |
| Flexural Stress | 330 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 11 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 305 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 325 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.00E-05 | -- | cm/cm/°C | |
| Transverse | 4.00E-05 | -- | cm/cm/°C | |
| Electrical | Dry | Conditioned | Unit | Test Method |
| Volume Resistivity | > 1.0E+15 | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.800 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Injection | Dry | Unit | ||
| Drying Temperature | 100 | °C | ||
| Drying Time | 4.0 to 8.0 | hr | ||
| Rear Temperature | 320 to 330 | °C | ||
| Middle Temperature | 325 to 335 | °C | ||
| Front Temperature | 330 to 335 | °C | ||
| Nozzle Temperature | 330 to 335 | °C | ||
| Processing (Melt) Temp | 330 to 340 | °C | ||
| Mold Temperature | 100 to 150 | °C | ||
| Injection Rate | Moderate-Fast | |||
| Back Pressure | 0.500 to 3.00 | MPa | ||
| Screw Compression Ratio | 2.5:1.0 | |||